Abstract
•The new lithium potassium borate glasses doped with Dy3+ were characterized by their physical and optical properties.•The glass samples features were obtained from XRD, FTIR, UV–vis–NIR and PL spectra measurements.•Glasses were exhibited a strong visible emission in blue and yellow region while a weak emission was observed in red region.
The luminescence, lasing and sensing properties of rare earth (RE) ions have drawn much interest among researchers. We have focussed on the physical and optical properties of Li2O–K2O–B2O3 (LKB) with different concentrations of dysprosium (Dy3+) ions. The glass samples were prepared using melt quenching method. The physical parameters of the prepared glass were determined. Optical measurements such as XRD, FTIR, absorption and photoluminescence spectra have been carried out. Dy3+: LKB glass showed eight absorption bands with hypersensitive transition located at 1265nm (6H15/2→6F11/2–6H9/2). Finally, Dy3+: LKB glass exhibited two intense luminescence emission at 481nm (4F9/2→6H15/2; blue) and 573nm (4F9/2→6H13/2; yellow) and feeble band at 683nm (4F9/2→6H11/2; red) with excitation wavelength at 370nm. The results obtained are prevalent with others studies and also point to its use in solid-state laser, optoelectronic devices and W-LEDs application.