Abstract
Optical localized heating in the nanoscale has recently attracted great attention due to its unique small hot spot size with high energy. However, the hot spot size is conventionally constrained by the diffraction limit. Plasmonic localized heating can provide solutions to this limitation in nanoscale patterning, cancer treatment, and data storage. Plasmonic approaches to overcome the diffraction limit in hot spot size have mainly utilized the excitation of surface plasmon or localized surface plasmon resonance. However, achieving plasmonic localized heating by the excitation of magnetic polariton has not been researched extensively yet. In this work, we numerically investigated the optical response of a nanoscale metamaterial composed of a gold nanowire array and a gold film separated by an ultrathin polymer spacer using ANSYS High Frequency Structural Simulator. A strong absorption peak at the wavelength of 760 nm was exhibited, and the underlying physical mechanism for the strong absorption was verified via the local electromagnetic field distribution to be magnetic resonance excitation. An inductor-capacitor circuit model was used to predict the magnetic resonance wavelength and compare with the numerical results for varied geometrical parameters. Volume loss density due to the strong local optical energy confinement was transferred as heat generation to an ANSYS thermal solver to obtain the local temperature profile. The steady state temperature profile shows an average temperature of 145 degrees C confined in a local area as small as 33 nm within the spacer, with a full-width at half-maximum of 50 nm along the x-direction. Moreover, the temperature rise from ambient drops to half its maximum value at a distance of 5 nm from the top of the spacer along the z-direction. This clearly demonstrates plasmonic localized heating beyond the diffraction limit via magnetic polariton excitation. Furthermore, the transient temperature profile shows that the system reached steady state within similar to 0.36 mu s. Published by AIP Publishing.