Abstract
Deformation characteristics were examined at temperatures of 875 and 925 C. The behavior was found to be extremely temperature dependent at these temperatures with critically resolved flow stresses ranging from 83 to 23 MPa. Despite the lower stresses encountered at 925 C, plastic behavior was limited to approximately 8 percent strain at both temperatures.