Abstract
Reversible addition–fragmentation chain transfer (RAFT) polymerizations were performed in the presence of organically modified clays and successfully prepared polystyrene-, poly(methyl methacrylate)-, and poly(n-butyl acrylate)-layered silicate nanocomposites. The polymers had well-defined molecular weights and low polydispersities, as expected from RAFT polymerizations. The morphology of polystyrene-, and poly(n-butyl acrylate)-nanocomposites were found to be exfoliated using montmorillonite modified with N,N-dimethyl-n-hexadecyl-(4-vinylbenzyl) ammonium (MMT-VB16). In the case of PMMA nanocomposite, the structure was a mixture of intercalated and exfoliated when MMT-VB16 was used, while the use of montmorillonite modified with 2-methacryloyloxyethyl-hexadecyldimethyl ammonium (MMT-MA16) resulted in exfoliation.