Abstract
► Single phase Ni0.5Cu0.25Zn0.25Fe2−xInxO4 ferrites were synthesized by citrate–nitrate precursor auto combustion. ► Magnetic properties decreased due to the substitution of In3+ ions. ► Dielectric properties decreased with increase in frequency. ► This composition can be used for multilayer chip inductor (MLCI) applications.
In submitted research; nanocrystalline powders having elements Ni0.5Cu0.25Zn0.25Fe2−xInxO4 with varied amounts of indium (x=0.0, 0.1, 0.2, 0.3 and 0.4) were grown-up by modified citrate to nitrate alchemy. The realism of single phase cubic spinel creation of the synthesized ferrite samples was studied by the DTA-TGA, XRD, SEM, EDX, FT-IR, VSM and dielectric measurements. SEM was applied to inspect the morphological variations and EDX was used to determine the compositional mass ratios. The studies on the dielectric constant (ε′), dielectric loss (ε″), loss tangent (tanδ), ac conductivity (σac), resistive and reactive parts of the impedance analysis (Z’ and Z”) at room temperature were also carried out. The saturation magnetizations (Ms) were determined using the vibrating sample magnetometer (VSM). Ms. decreased with the increase In3+ doping content, as Fe3+ of 5μB ions are replaced by In3+ of 0μB ions.