Abstract
► Acrylic acid was grafted on hydroxyethyl cellulose using redox initiation system. ► The polymerization was carried out under a variety of reaction conditions. ► Maximum conversion obtained at equimolar ratio of the redox system components.
Poly(acrylic acid) hydroxyethyl cellulose [poly(AA)-HEC] graft copolymer was prepared by polymerizing acrylic acid (AA) with hydroxyethyl cellulose (HEC) using potassium bromate/thiourea dioxide (KBrO3/TUD) as redox initiation system. The polymerization reaction was carried out under a variety of conditions including concentrations of AA, KBrO3 and TUD, material to liquor ratio and polymerization temperature. The polymerization reaction was monitored by withdrawing samples from the reaction medium and measuring the total conversion. The rheological properties of the poly(AA)-HEC graft copolymer were investigated. The total conversion and rheological properties of the graft copolymer depended on the ratio of KBrO3 to TUD and on acrylic acid concentration as well as temperature and material to liquor ratio. Optimum conditions of the graft copolymer preparation were 30mmol KBrO3 and 30mmol TUD/100g HEC, 100% AA (based on weight of HEC), duration 2h at temperature 50°C using a material to liquor ratio of 1:10.