Abstract
Alumina nanoparticles were prepared by sol-gel method, where the obtained nanosize was 35 nm, and the nanomaterial was coated with PVP polymer, where the nanomaterial was dispersed by ultrasonic waves for half an hour, and then, the polymer was added, and under high magnetic stirring for 24 hours, it was dried at a temperature of 60 degrees C for 24 hours. Cadmium salt solutions were prepared with different concentrations of 10, 30, and 60 ppm, and the nanomaterial was immersed in the prepared solutions at different times of 10, 30, and 60 minutes, and the measurement was done by an atomic absorption device. By means of the electronic scanner, a difference appeared in the nanosize, and this indicates that the packaging has completely occurred.