Abstract
Objective: This was an in vitro evaluation of push-out bond strength and surface microhardness of calcium silicate-based biomaterials in coronal and apical root dentin. Materials and Methods: Ninety sections (2 mm thick) of coronal and apical root dentin were obtained from roots of 60 extracted teeth; the canals were enlarged to a standardized cavity diameter of 1.3 mm. Sections were randomly divided into 6 groups (n = 15 per group), and cavities were filled with Biodentine TM, BioAggregate, or ProRoot mineral trioxide aggregate (MTA), according to the manufacturers' instructions. Push-out bond strength values were measured using a universal testing machine under a compressive load at a speed of 1 mm/min. Samples were analyzed under a light microscope to determine the nature of bond failure. Ten samples (2 mm thick) were prepared for all the materials, and Vickers microhardness was determined using a digital hardness tester. Data were analyzed using one-way analysis of variance and Tukey-Kramer multiple comparison tests at a significance level of p < 0.05. Results: Biodentine (42.02; 39.35 MPa) and ProRoot MTA (21.86; 34.13 MPa) showed significantly higher bond strengths than BioAggregate (6.63; 10.09 MPa) in coronal and apical root dentin, respectively (p < 0.05). Biodentine also differed significantly from ProRoot MTA in coronal dentin. Bond failure was predominantly adhesive in Biodentine and ProRoot MTA, while BioAggregate showed predominantly mixed failure. ProRoot MTA (158.52 HV) showed significantly higher microhardness and BioAggregate (68.79 HV) showed the lowest hardness. Conclusion: Biodentine and ProRoot MTA showed higher bond strength and microhardness compared to BioAggregate. (C) 2016 S. Karger AG, Basel