Abstract
This study examines the restoration of waste plastic polymers based on LDPE, HDPE or PP through dissolution/reprecipitation. Experimental conditions of the recycling process, including type of solvent/non-solvent, original polymer concentration and dissolution temperature were optimized. The results revealed that by using different prepared solvents/non-solvents at various ratios and temperatures, the polymer recovery was always greater than 94%. The FTIR spectra and the thermal properties (melting point and crystallinity) of the polymers before and after recycling were measured using differential scanning calorimetry (DSC). Mechanical properties of the waste polymer before and after recycling were also measured. Besides small occasional deviations, the properties did not change. The tensile strength at maximum load was 71, 18.8, and 74 MPa for the recycled LDPE, HDPE and PP, respectively, and 7.78, 18.54 and 786 MPa for the virgin polymer. For the waste, the strength was 6.2, 15.58 and 6.76 MPa.