Abstract
The aim of this in vitro investigation was to assess and compare surface characteristics and nanomechanics of model polymer infiltrated ceramic network (PICN) materials compared to CAD/CAM resin composite blocks.
Four model PICN materials sintered at different temperatures (Exp.125, Exp.130, Exp.135 and Exp.155) were investigated along with three CAD/CAM resin composites; Lava Ultimate (LU), Cerasmart (CS) and Grandio Bloc (GB), and one commercial PICN block - Vita Enamic (VE). Forty samples were prepared with dimensions of 14 × 12 × 2 mm for resin ceramic and VE blocks and 15 × 2 mm discs for model PICN materials. All samples were scanned using atomic force microscopy (AFM) (n = 3) at multiple locations and two different scan sizes (20 ×20 µm and 3 ×3 µm). Surface optical gloss (n = 5) at 60° was also determined for all the groups. Data were analysed using one-way ANOVA, and Tukey’s post hoc test (α = 0.05).
Resin composite blocks showed smoother surfaces compared to the PICN materials. The average surface roughness values (Ra) ranged from 7.75 nm to 31.21 nm and the gloss value ranged from 56.43 GU to 91.81 GU. The highest surface roughness value was found for Exp.125 (31.21 nm) while LU showed the lowest roughness value (7.75 nm) (the difference being statistically significant: p = 0.001). Variation was noticed in terms of nanomechanical mapping within and between the groups. Images generated from the elastic modulus map values clearly indicated that all PICN materials had more than one phase and very different components.
CAD/CAM resin composite blocks exhibited higher gloss and lower roughness values compared to PICN materials. However, both the commercial and model PICN materials showed more stiffness than resin composite with the presence of at least two different phases. Sintering temperature appears to have a significant effect on material topography and nanomechanical properties. The model PICN sintered at 1550 °C showed a comparable range of elastic modulus values to those of enamel.