Abstract
This paper concerns the importance of the preparation of the targets that may be used for pulsed laser deposition of iron-doped indium oxide films. Targets with a fixed concentration of iron are fabricated from indium oxide and iron metal or one of the oxides of iron, FeO, Fe3O4 and Fe2O3. Films from each target were ablated onto sapphire substrates at the same temperature under different oxygen pressures such that the thickness of the films was kept approximately constant. The films were studied using X-ray diffraction, X-ray absorption (both XANES and EXAFS), optical absorption and magnetic circular dichroism. The magnetic properties were measured with a SQUID magnetometer. At the lowest oxygen pressure, there was evidence that some of the iron ions in the films were in the state Fe2+, rather than Fe3+, and there was also a little metallic iron; these properties were accompanied by a substantial magnetisation. As the amount of the oxygen was increased, the number of defect phases and the saturation magnetisation was reduced and the band gap increased. In each case, we found that the amount of the oxygen that had been included in the target from the precursor added to the effect of adding oxygen in the deposition chamber. It was concluded that the amount of oxygen in the target due to the precursor was an important consideration but not a defining factor in the quality of the films.