Abstract
Formation of complex salts (oxychlorides) has been suspected for causing chemical degradation of concrete in cold regions. In this study, conditioned mode (controlled temperature and relative humidity) environmental scanning electron microscopy was specifically used to minimize changes in the crystal structures of oxychlorides phases and thus reliably capture their unaltered morphology and existence/effects on concrete exposed to different de-icing salts under two different environmental conditions (constant low temperature and wetting/drying (W/D) cycles). Formation of acicular flattened blades of 3- and 5-form magnesium oxychloride (MOX) and tiny fibrous crystals as well as subhedral pseudo-hexagonal calcium oxychloride plates (COX) were found in deteriorated concrete specimens, depending on the type of solution. The reversible formation of hydrous and anhydrous COX during W/D cycles had a significant effect on aggravating the kinetics of damage of concrete in this exposure. The combined salt (MgCl2+CaCl2), which simulates using a synergistic maintenance and protective strategy for concrete pavements in winter, was the most aggressive solution; thus, this practice should be cautiously reconsidered. The incorporation of 30% fly ash had a pronounced effect on improving the concrete resistance to damage as reflected by sound mechanical properties and longevity. Also, the performance of concrete was much enhanced when an innovative supplementary cementitious material, nanosilica, was incorporated in the cementitious system.