Abstract
Superhydrophobic cotton fabrics were prepared via a facile and environmentally friendly strategy to deposit an organically modified silica aerogel (ormosil) thin film onto the fabrics first, followed by polydimethylsiloxane (PDMS) topcoating. The PDMS-ormosil coating displayed a uniform 3D fractal-like structure with numerous loose micro-scale pores, white the PDMS layer increased the binding strength of the hierarchical ormosil film to form a highly robust porous network on the fibers. In comparison with hydrophilic cotton fabrics, the modified cotton fabric exhibited a highly superhydrophobic activity with a water contact angle higher than 160 degrees and a sliding angle lower than 10 degrees. The as-constructed PDMS-ormosil@fabrics are able to withstand 100 cycles of abrasion and 5 cycles of accelerated machine wash without an apparent decrease of superhydrophobicity. In addition, the superhydrophobic cotton fabrics are very stable in strongly acidic and alkaline solutions. Furthermore, the superhydrophobic coating has no or negligible adverse effect on the important textile physical properties of the cotton fabric, such as the strength, air permeability, and flexibility. The composite super-antiwetting fabrics have demonstrated excellent anti-fouling, self-cleaning ability and are highly efficient in oil-water separation for various oil-water mixtures. This facile synthesis technique has the advantages of scalable fabrication of multifunctional fabrics for potential applications in self-cleaning and versatile water-oil separation.