Abstract
Ce3+ is proved to play a major role in improving the UV light excitation and thermal stability performance of Sm3+ via ET of Ce3+ to Sm3+. The SrLa0.95Al3B4O15:0.02Ce3+,0.03Sm3+ phosphors possess significant resistance to thermal quenching. Practical application such as UV-LED devices owned warm white emission with the low CCT 4503 K, high CRI~88.
[Display omitted]
•The synthesized phosphors possess significant resistance to the thermal-quenching.•The red emission intensity of Ce3+,Sm3+ is enhanced up to ~3.9 times compared to the pure SLAB:Sm3+.•Phosphors have satisfactory IQE (up to 74.3%) and absorption efficiency (76.5%).•LED devices were fabricated owned warm white emission with the low CCT 4503 K, high CRI (Ra~88).
Ce3+ ion can effectively sensitize Sm3+ ion via energy transfer, and this phenomenon can led to the development of white light-emitting diodes (WLED). However, interestingly, high correlated color temperature (CCT), poor color-rending index (CRI), poor thermal stability, and low efficacy of available red phosphor still pose immense challenges. Herein, we undertook a combined analysis: X-ray diffraction (XRD), crystal refinement, electron spin resonance (ESR), transmission electron microscopy (TEM), scanning electron microscopy (SEM), and diffuse reflection spectroscopy (DRS). We also observed the optical properties of the resulting samples. The Ce3+ and Sm3+ dopants on the Sr2+ and La3+ sites in the mixed cation borate Sr3LaAl3B4O15 (SLAB) phosphors were quantitatively evaluated. A cerium ion merged as a sensitizer, improving the red emission intensity by enhancing it 3.9 times. The energy transfer (ET) between Ce3+ and Sm3+ was examined experimentally and with theoretical models as a function of Ce3+ concentrations at ambient temperatures. Several theoretical models were employed to simulate the luminescence decays of Ce3+ and Sm3+ doped samples at different doping levels and their transfer mechanisms were studied depending on forced electric dipole at each ion. Notably, the electronic sites created by the oxygen vacancies around the Ln3+ ions can effectively justify the highly efficient bluish-red phosphor. Additionally, the SL0.95AB:0.02Ce3+,0.03Sm3+ exhibited outstanding thermal-quenching (TQ) resistance and has > 94.8% intensity at 425 K. WLEDs made with the use of SL0.95AB:0.02Ce3+,0.03Sm3+ furnished an exceptional CRI exceeding 88 and low at CCT 4503 K. These results are superior to the parameters of commercial WLED containing Y3Al5O12:Ce3+ phosphor and blue LED chip (CCT≈7746 K, CRI≈75), and they could be a cornerstone for the fabrication of warm WLEDs.