Abstract
In this work, we investigate the susceptibility of Ni-Ti superelastic wires to the strain rates during tensile testing after hydrogen charging. Cathodic hydrogen charging is performed at a current density of 10 A/m² during 2-12 h in 0.9% NaCl solution and aged for 24 h at room temperature. Specimens underwent one cycle of loading-unloading reaching a stress value of 700 MPa. During loading, strain rates from 10
−6
to 5 × 10
−2
s
−1
have been achieved. After 8 h of hydrogen charging, an embrittlement has been detected in the tensile strain rate range of 10
−6
to 10
−4
s
−1
. In contrast, no embrittlement has been detected for strain rates of 10
−3
s
−1
and higher. However, after 12 h of hydrogen charging and 24 h of annealing at room temperature, the embrittlement occurs in the beginning of the austenite-martensite transformation for all the studied strain rate values. These results show that for a range of critical amounts of diffused hydrogen, the embrittlement of the Ni-Ti superelastic alloy strongly depends on the strain rate during the tensile test. Moreover, it has been shown that this embrittlement occurs for low values of strain rates rather than the higher ones. This behaviour is attributed to the interaction between the diffused hydrogen and growth of the martensitic domain.