Abstract
This study pertains to incorporation of coffee silverskin (CSS) in partial replacement for ordinary Portland cement (OPC) in mortar, by investigating its fresh properties (setting and workability), compressive strength (3, 7, 14 and 28-day), absorption and microstructural characteristics. The objectives were to reduce environmental solid wastes and achieve cost efficiency in the use of construction materials. The CSS was expressed as a ratio of total binder (CSS/(OPC + CSS)) and varied from 0 to 5%. The findings revealed that CSS could reduce workability, setting time and early strength. It could also enhance the absorption of the CSS-blended mortar (CBM). The cause of reduction in workability was due to its contribution to the viscosity of the mixture due to the emulsification of the fat component (acetate) and aromatic compounds, as observed in the Fourier Transform Infrared (FTIR) spectroscopy and X-ray diffraction techniques. The presence of these compounds also caused microstructural disintegration that resulted in the lower strength. In addition, the presence of other organic compound in CSS but absent in OPC enhanced microstructural disintegration and porosity in CBM. The 28-day strength of 25 MPa could be achieved in CSS-blended mortar if the CSS/(CSS + OPC) ratios were kept below 3%. The maximum compressive strength of 38.5 MPa was obtained with the optimum CSS content of 1 wt%. The relative density (water) of CSS was 0.345; therefore, it could also be used to produce lightweight concrete. This study promotes the valorization of raw CSS waste as construction material which could be used for subgrade in the construction of road pavement.