Abstract
Chemical co-precipitation route adopted to synthesize the magnetic materials. In the present work, iron is replaced by ytterbium ion in manganese-based spinel ferrites. The yield chemically represented by MnYb (x) Fe2-x O-4 (x = 0.00, 0.025, 0.05, 0.075, 0.10) and its structural, magnetic and electrical properties were observed. The cubic structure of spinel ferrites was confirmed by X-ray diffraction analysis. Spherically shaped grains were perceived in SEM pictures and size lessened with the growth of ytterbium concentration. SEM profile also shows little irregularity in spherical particles. The substitution of ytterbium (Yb) results in the enhancement of electrical resistivity. The resistivity was reduced with the gradual increase in temperature from 303 to 693 K. The trend of activation energy was found to be similar to that of room temperature resistivity. The coercivity of samples was raised with Yb-ion substitution while saturation magnetization and remanence reduced.