Abstract
ZnO nanoparticles were synthesized by direct precipitation method at ambient conditions. Structural, thermal, morphological and optical properties of ZnO nanoparticles were investigated by X-ray diffraction (XRD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), Ultraviolet-Visible spectroscopy and Raman spectroscopy. The XRD measurement shows that ZnO powder has a wurtzite structure. The grain size was estimated from Scherer's method and Williamson-Hall (W-H) plots. From DSC curve we can deduce the various endothermic and exothermic peaks obtained when the sample was heated from room temperature to 413 degrees C. The morphology and grain distribution of ZnO nanopartides were analyzed by SEM. Optical properties were investigated by UV-Visible spectroscopy. The Tauc model was used to determine the optical gap energy of the synthesized ZnO particles. The observed Raman peak at 438 cm(-1) was attributed to the E-2 (high) mode. The broad band at 569 cm(-1) is due to disorder-activated Raman scattering for A(1) mode. These bands are associated with the first-order Raman active modes of the ZnO phase. (C) 2015 Elsevier Ltd. All rights reserved.