Abstract
Nanostructures (NSs) of basic composition Sn1−xFex/2Cox/2O2 with x=0.00, 0.04, 0.06, 0.08 and 0.1 were synthesized by citrate-gel route and characterized to understand their structural, electrical and magnetic properties. X-ray diffraction and Raman spectroscopy were used to confirm the formation of single phase rutile type tetragonal structure. The crystallite sizes calculated by using Williamson Hall were found to decrease with increasing doping level. In addition to the fundamental Raman peaks of rutile SnO2, the other three weak Raman peaks at about 505, 537 and 688cm−1 were also observed. Field emission scanning electron microscopy studies showed the emergence of structural transformation. Electric properties such as dc electrical resistivity as a function of temperature and ac conductivity as a function of frequency were also studied. The variation of dielectric properties with frequency reveals that the dispersion is due to Maxwell–Wagner type of interfacial polarization in general. Hysteresis loops were clearly observed in M–H curves of Fe and Co co-doped SnO2 NSs. However, pure SnO2 nanoparticles (NPs) showed paramagnetic behaviour which vanished at higher values of magnetic field. The grain and grain boundary contribution in the conduction process is estimated through complex impedance plot fitted with non-linear least square (NLLS) approach which shows that the role of grain boundaries increases rapidly as compared to the grain volume with the increase of Fe and Co ions in to system.
[Display omitted]
•Synthesis of Fe and Co co-doped SnO2 nanostructures through Citrate-gel method.•Structural analysis of as prepared nanostructures using XRD, Raman, SEM and EDS.•Dielectric properties for all the samples with frequency at room temperature.•Resistivity measurements in the temperature range of 297–400K.•M–H curves for Sn1−xFex/2Cox/2O2 nanorods at room temperature using VSM.