Abstract
•Nano ferrite Mg0.5Zn0.5−xCuxFe2O4 were prepared through co-precipitation route.•Structural investigations of XRD and FTIR revealed formation of spinel structure.•Lattice constant decrease while saturation magnetization increase.•Correlated barrier-hopping (CBH) is the dominant conduction mechanism.•Dielectric properties make sample appropriate for multilayer inductor applications.
Nano-crystalline Mg0.5Zn0.5−xCuxFe2O4 (x=0.0, 0.1, 0.2, 0.3, 0.4 and 0.5) ferrite powders were synthesized using co-precipitation method. The influence of Cu2+ ions substitution on the structural and magnetic properties was investigated. X-ray diffraction measurements revealed the formation of nano-crystalline ferrite with single cubic spinel phase. The lattice constant was found to decrease with increasing Cu2+ ions content. Infrared spectral analysis confirmed formation of the spinel structure for the respective ferrite system. Magnetic data showed that the saturation magnetization (Ms) increases with Cu2+ concentration up to x=0.2 and then decreases with further increase of Cu2+ ions in this ferrite system. The proposed cation distribution deduced from X-ray diffraction, infrared spectra and magnetization data indicated mixed ferrite type. Dielectric constants ε′, dielectric loss ε′′, dielectric loss tangent tanδ and ac conductivity, σac, were investigated as a function of frequency and temperature. Influence of Cu2+ substation on the ac conductivity exhibited significant behavior at low frequencies and low temperatures, T⩽100°C. Both dielectric constants (ε′, ε″) found to increase with the increase of the temperature. At low temperatures, dielectric loss tanδ indicated a decrease with frequency with slight change at high temperatures.