Abstract
The nanocomposites of the polyaniline and Co1−xCuxFe2O4 (PANI/CoCuFe) were prepared by in-situ oxidative polymerization of aniline. Prepared nanocomposites samples were characterized by using various experimental techniques like X-ray diffraction (XRD), Fourier transformed infrared spectroscopy (FT-IR), field emission scanning electron microscope (FE-SEM), vibrating sample magnetometer (VSM), Mössbauer spectroscopy and ultraviolet–visible spectrophotometry (UV–VIS). The elemental analysis as obtained from the energy dispersive X-ray spectroscopy (EDAX) measurement is in close agreement with the expected composition from the stoichiometry of the reactant solutions. XRD result confirms that all the samples have the single phase cubic spinel structure. Unit cell parameter ‘a’ is found to decrease with the increase in copper ion substitution. The crystallite size was investigated by using the Debye–Scherer formula and it was found in the range of ∼28–37 nm. FE-SEM confirmed the homogeneous and well defined surface morphology of the synthesized samples. FT-IR study showed the main absorption bands corresponding to the spinel structure those arose due to the tetrahedral and octahedral stretching vibrations. Cation distribution was estimated using XRD data. Hysteresis measurements revealed that the saturation magnetization decreased with increase in Cu2+ substitution. Magnetic environment of 57Fe in Cu-doped cobalt ferrite was investigated by using Mössbauer spectroscopy. Mössbauer study evidenced the ferrimagnetic behavior of the synthesized samples.
•Crystallite size decreases with increasing Cu2+ substitution.•The prepared samples show the formation of single phase cubic spinel structure.•Cation distribution shows that Cu and Co ions shows strong preference toward octahedral B site.•Magnetization decreases with increasing Cu2+ substitution.•Mössbauer study shows ferrimagnetic behavior of the samples.
[Display omitted]