Abstract
For improving the hydrolytic stability of sulfonated polyimides consisting of five membered anhydrides, novel sulfonated polyimides (NSPIs) were prepared via polymerization of 3,3 & PRIME;,4,4 & PRIME;-benzophenonetetracarboxylic dianhydride (BTDA), with a novel diamine monomer with a pendant sulfonic acid group and 4,4-oxydianiline. Water uptake of this NSPI with an excellent film-forming ability was almost equal to that of Nafion(R) 117, while their ion exchange capacity (IEC) was 22% higher than Nafion(R) 117. The loss in weight decreased by 53% and loss in IEC decreased by 66% compared to that of Nafion(R) 117; both were used to quantitatively measure hydrolytic stability, and radical oxidative stability also increased by 75% when compared with Nafion(R) 117. Mechanically, this NSPI was superior, and its proton conductivity was higher than Nafion(R) 117 at elevated temperatures. All these improvements were due to the introduction of this pendant group. Taken together, we herein report a promising renewable energy source based on SPIs capable of displaying proton conductivity and enhanced hydrophilicity.