Abstract
The effect of sulfate content and calcination temperature on the structure, acidity and catalytic activity of tin oxide was investigated. Sulfated tin oxide samples were characterized by thermal analysis (DTA and TGA), powder X-ray diffraction (XRD) and N-2 adsorption at -196 degrees C. The surface acidity was measured by Potentiometric titration, DSC-TGA and FT-IR techniques. The catalytic performance was evaluated on the esterification of acetic acid with amyl alcohol in the vapor phase between 150 and 250 degrees C. XRD measurements show that the sulfating of SnO2 tends to hinder the crystallization of SnO2 and inhibits crystal growth. It was found that the surface acidity increases with the increase of thermal treatment up to 550 degrees C, while the further increase of calcination temperature beyond 750 degrees C leads to a decrease of acid sites and acid sites strength. The addition of sulfate to SnO2, brings about ail increase of the specific surface area, whereas the calcination temperature exhibits a reverse trend. The formation of amyl acetate increases with increase of surface acidities. Lewis and Bronsted acid sites appears to be needed for catalytic activity in amyl acetate formation, both are maximum when the sulfate content and calcination temperature are 30 wt.% and 550 degrees C, respectively. (c) 2007 Elsevier B.V. All rights reserved.