Abstract
Tungsten oxide (WO3), MXene, and an WO3/MXene nanocomposite were synthesized to study their photocatalytic and biological applications. Tungsten oxide was synthesized by an easy and cost-effective hydrothermal method, and its composite with MXene was prepared through the sonication method. The synthesized tungsten oxide, MXene, and its composite were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), Fourier transform infrared (FTIR), energy-dispersive X-ray analysis (EDX), and Brunauer-Emmett-Teller (BET) for their structural, morphological, spectral, elemental and surface area analysis, respectively. The crystallite size of WO3 calculated from XRD was similar to 10 nm, the particle size of WO3 was 130 nm, and the average thickness of MXene layers was 175 nm, which was calculated from FESEM. The photocatalytic activity of as-synthesized samples was carried out for the degradation of methylene blue under solar radiation, MXene, the WO3/MXene composite, and WO3 exhibited 54%, 89%, and 99% photocatalytic degradation, respectively. WO3 showed maximal degradation ability; by adding WO3 to MXene, the degradation ability of MXene was enhanced. Studies on antibacterial activity demonstrated that these samples are good antibacterial agents against positive strains, and their antibacterial activity against negative strains depends upon their concentration. Against positive strains, the WO3/MXene composite's inhibition zone was at 7 mm, while it became 9 mm upon increasing the concentration. This study proves thatWO(3), MXene, and theWO(3)/MXene nanocomposite could be used in biological and environmental applications.