Abstract
This study intends to synthesis novel compound phenolic chitosan-based via reaction of chitosan with 2-Chloro-N-phenylacetamide in 1-butyl-3-methylimidazolium chloride ionic liquid in the presence of pyridine at 80 degrees C for 4 h. The alterations in the chemical structure and morphology of the chitosan-N-phenylacetamide biopolymer were verified using IR spectroscopy, XRD, and SEM analyses. Chitosan and Chitosan-N-phenyacetamide were subjected to thermo-gravimetric analysis under an inert atmosphere in the temperature range of room temperature - 600 degrees C at a heating rate of 20 degrees C.min(-1). The kinetic parameters were determined by the Coats-Redfern method. The corresponding kinetic parameters of the main degradation stages were also determined. The energy required for the degradation of pure chitosan was lower than that of chitosan-N-phenylacetamide in the first region of thermal degradation where the main pyrolysis reaction took place, and the largest weight loss occurred. Energy values in this region are running from 40.25 to 151.07 kJ/mol and 58.45 to 210.99 kJ/mol, respectively. The most probable reaction functions have thus been determined for these two stages by Coats-Redfern and Criado method, leading to greatly improved calculation performance over the entire conversion range. The pyrolysis reaction models of both pure chitosan and chitosan-N-phenylacetamide are described by the reaction, second-order F2.