Abstract
The poly(ethylene) glycol (PEG) capped mancozeb nanoformulation was prepared by the ultrasonic method using a 1% mancozeb solution and 20% capping agent, PEG-4000. The synthesized nanoformulation was characterized using UV-visible, FTIR, SEM and TEM techniques. The photolytic and photo catalytic experiments were carried out in a Borosil glass bottle in the presence of sunlight, varying the pH proportions at a single fortification level (1.0 g/mL) in ground water, under sunlight. The optimal catalyst concentration for complete degradation was observed to be 0.1 percent. The mancozeb nanoformulation in water was determined using the HPLC-PDA method, and the rate constant and the 50% degradation (DT50) values were calculated based on the results. The photolytic results show that there is no significant loss of residues due to adsorption. Titanium dioxide (TiO2) was discovered to be an excellent decontaminating catalyst in a variety of water samples. The compound survives for several days in the absence of a catalyst.