Abstract
Ricinus communis (RC) oil-based materials are currently receiving increasing attention because of economic and environmental concerns. In the present work, RC oil-a natural triol has been utilized for the development of an advanced polymeric material-poly(urethane-ricinoleamide) (PUR) through very simple synthesis and curing strategy, omitting derivatization steps or side reactions, chain extenders and crosslinkers. The synthesis of PUR was carried out in two steps. The first step is the introduction of an amide group in the RC oil (89.5% ricinoleic acid) via base catalyzed amidation, which results in N, N-bis (2-hydroxyethyl) ricinoleamide (HERA). The second step is urethanation of HERA by the reaction of toluene-2,4-diisocyanate (TDI) in minimal possible organic solvent by one-shot technique, which results in the formation of polyurethane along with amide linkages. The physico-chemical and spectral studies (FT-IR, H-1-NMR and C-13-NMR techniques) confirm these two reactions and the structure of PUR. The resin was cured at ambient temperature without any cross linker. Solubility of the resin was investigated in different polar and non-polar solvents. Thermo-gravimetric analysis (TGA)/differential thermal analysis (DTA) and Differential Scanning Calorimetry (DSC) were used to determine the thermal stability and curing behavior of PUR. An ambient cured ricinoleamide modified polyurethane resin exhibited thermal resistance up to 200-220 A degrees C.