Abstract
A newly designed carbocyclic pseudo Tröger's base diamine (CTB) monomer, 2,8-dimethyl-3,9-diamino-5,6,11,12-tetrahydro-5,11-methanodibenzo[a,e][8]annulene (CTBDA) and its isomeric analogue 2,8-dimethyl-(1,7)(4,10)(3,9)-diamino-5,6,11,12-tetrahydro-5,11-methanodibenzo[a,e][8]annulene (iCTBDA), were designed for the synthesis of microporous 6FDA-based polyimides (6FDA-CTBDA and 6FDA-iCTBDA). Both polyimides were soluble, exhibited excellent thermal stability of ∼490 °C, and had high surface areas of 587 m2 g−1 (6FDA-CTBDA) and 562 m2 g−1 (6FDA-iCTBDA). A 6FDA-based polyimide derived from 4,10-dimethyl-3,9-diamino-6H,12H-5,11-methanodibenzo[b,f][1,5]-diazocine (6FDA-TBDA) was made for comparison to investigate the effects of the basic tertiary nitrogen functionality in the Tröger's base diamine on the polymer properties relative to the carbocyclic 6FDA-CTBDA analogue. 6FDA-TBDA displayed lower gas permeabilities but moderately higher gas-pair permselectivities than 6FDA-CTBDA. The enhanced permselectivity of 6FDA-TBDA resulted exclusively from higher diffusion-based selectivity. Direct gas sorption measurements demonstrated that the basicity in the Tröger's base bridge moiety enhanced the sorption capacity of CO2 only slightly and had no effect on the CO2/CH4 solubility selectivity in 6FDA-TBDA vs. 6FDA-CTBDA.
[Display omitted]
•A novel carbocyclic pseudo Tröger's base diamine (CTBDA) was designed.•Fresh 6FDA-CTBDA showed BET surface area of 587 m2 g−1 with CO2 permeability of 291 Barrer and CO2/CH4 selectivity of 25.•60-day aging of 6FDA-CTBDA led to decrease in CO2 permeability to 201 Barrer with increase in CO2/CH4 selectivity to 28.•Tertiary amine groups in the Tröger's base polyimide had essentially no effect on CO2/CH4 solubility selectivity.