Abstract
The burning of fossil fuels produces carbon dioxide emissions, increased levels of which cause serious environmental problems. Therefore, the design and use of new materials as media for capturing carbon dioxide and other gases, such as hydrogen and methane, has attracted significant research attention. In this work, three metal complexes containing a fusidate moiety were synthesized and tested as storage media for gases. By reacting sodium fusidate and metal chlorides in boiling ethanol, the corresponding metal complexes were obtained with 69-76% yields. The fusidate moiety acts as a bidentate ligand with variable geometry (distortion octahedral, square planner, or tetrahedral) depending on the metal (manganese, copper, or zinc, respectively) it is associated with. The elemental composition of the metal complexes was confirmed via energy dispersive X-ray spectroscopy and their surface morphology was inspected via field emission scanning electron microscopy. The Brunauer-Emmett-Teller surface area of the metal complexes varied from 31.2 to 46.9 m(2)/g, with pore volume and diameters of 0.035-0.049 cm(3)/g and 3.02-3.18 nm, respectively. The gas uptake at 323 K for carbon dioxide, hydrogen, and methane depended on the metal, gas, surface pore volume, and pore diameter. Reasonable carbon dioxide uptake (6.3-7.2wt%) was achieved with fusidate metal complexes at high temperature and pressure, whereas hydrogen and methane slowly permeated throughout the complexes.