Abstract
The modification and tailoring characteristics of nanostructured materials are of great interest due to controllable and unusual inherent properties in such materials. A simple spray pyrolysis technique was used to prepare pure and La-doped ZnO films. The influence of La concentration (0, 0.33, 0.45, 0.66, 0.92 and 1.04 at. %) on the structural, optical, and magnetic properties of ZnO was investigated. The exact nominal compositions of the prepared films were determined from the field emission scanning electron microscope occupied with EDX. X-ray diffraction confirmed that the samples possessed single-phase hexagonal wurtzite structure. The main crystal size was decreased from 315.50 angstrom to 229.04 angstrom depending on La dopant concentration. This decrease is due to the small ionic radius of Zn ions in compared to La ions. The band gap values were found to be depend strongly on La3+ ion content. Introducing La into ZnO induces a clear magnetic moment without any distortion in the geometrical symmetry, it also reveals the ferromagnetic coupling. The saturation magnetic moment of 1.04 at.% La-doped ZnO shows the highest value of 0.014 emu, which is similar to 23 times higher than pure ZnO sample. The obtained results were discussed and compared with other literature data and showed an acceptable agreement. (C) 2019 Elsevier B.V. All rights reserved.