Abstract
This study reports on the activity and stability of PdO/gamma-AlOOH/gamma-Al2O3 monolith catalysts, promoted with varying amounts of CeO2, for CH4 oxidation. Although the beneficial effects of CeO2 have been reported for powdered catalysts, this study used a cordierite (2MgO.2Al(2)O(3).5SiO(2)) mini-monolith (400 cells per square inch, 1 cm diameter x 2.5 cm length; similar to 52 cells), washcoated with a suspension of gamma-Al2O3 combined with boehmite (gamma-AlOOH), followed by sequential deposition of Ce and Pd (0.5 wt.%) by wetness impregnation. The monolith catalysts' CH4 oxidation activity and stability were assessed in the presence of CO, CO2, H2O and SO2 at low temperature (<= 550 degrees C), relevant to emission control from lean-burn natural gas vehicles (NGVs). The CeO2 loading (0 to 4 wt.%) did not significantly impact the adhesion and thermal stability of the washcoat, but CeO2 reduced the inhibition of CH4 oxidation by H2O and SO2. The catalyst activity, measured by temperature-programmed methane oxidation (TPO) in a dry feed gas with 0.07 vol.% CH4, showed that adding CeO2 to the gamma-AlOOH/gamma-Al2O3 washcoat suppressed the activity of the catalysts; whereas, CeO2 improved the catalyst activity when H2O (2 and 5 vol.%) was present in the feed gas. Moreover, adding CeO2 decreased catalyst deactivation that occurred in the presence of 10 vol.% H2O and 5 ppmv SO2 at 500 degrees C, measured over a 25 h time-on-stream (TOS) period. The highest catalyst activity and stability for CH4 oxidation in the presence of H2O was obtained by adding 2 wt.% CeO2 to the washcoat.