Abstract
The generation, detection and measurement of laser-induced carbon plasma ions and their implantation effects on brass substrate have been investigated. Thomson parabola technique was employed to measure the energy and flux of carbon ions. The magnetic field of strength 80 mT was applied on the graphite plasma plume to provide an appropriate trajectory to the generated ions. The energy of carbon ions is 678 KeV for laser fluence of 5.1 J/cm(2) which was kept constant for all exposures. The flux of ions varies from 32x10(11) to 72x10(14) ions/cm(2) for varying numbers of laser pulses from 3000 to 12,000. In order to explore the ion irradiation effects on brass, four brass substrates were irradiated by carbon ions of different flux. Scanning electron microscope (SEM) and X-ray diffractometer (XRD) are used to analyze the surface morphology and crystallographic structure of ion-implanted brass, respectively. SEM analysis reveals the formation and growth of nano-/micro-sized cavities, pores and pits for the various ion flux for varying numbers of laser pulses from 3000 to 12,000. By increasing ion flux by increasing the number of pulses up to 9000 shots, the dendritic structures initiate to grow along with cavities and pores. At the maximum ion flux for 12,000 shots, the unequiaxed dendritic structures become distinct and the distance between the dendrites is decreased, whereas cavities, pores and pits are completely finished. The XRD analysis reveals that a new phase of ZnC (0012) is formed in the brass substrate after ion implantation. Universal tensile testing machine and Vickers microhardness tester are used to explore the yield stress, ultimate tensile strength and microhardness of ion-implanted brass substrate. The mechanical properties monotonically increase by increasing the ion flux. Variations in mechanical properties are correlated with surface and structural modifications of brass.