Abstract
The aim of the study was to assess the effect of delayed photoinitiation on the polymerization contraction stress (PCS) and degree of conversion (DC) of a dual-cure resin-luting agent. Thirty-five disk (6 mm x 1 mm) samples (n = 10 each group) of dual cure resin luting agent for PCS assessment were fabricated and polymerized using two illuminated quartz rods. Based on the delay in photoinitiation, 30 disks were divided among six groups [group A-0 min (min) delay, group B-2 min, group C-4 min, group D-6 min, group E-8 min and group F-10 min]. A non-photoinitiated group (group G - chemical cure - n = 5) was included as control. The PCS for all specimens was assessed using a Tensometer. For DC evaluation thirty-five specimens were divided into seven groups with delays in photo-initiation (group H-0 min, group I-2 min, group J-4 min, group K-6 min, group L-8 min and group M-10 min, group N-chemical cure). DC was assessed using attenuated total reflectance spectroscopic technique. Statistical comparison among groups was performed using analysis of variance (a = 0.05). The maximum and minimum PCS and DC values with delayed photo-initiation was observed in group-C (3.34 MPa) & group-F (2.44 MPa); and group-M (0.78 MPa) and group-H (0.55 MPa) respectively. Chemically cured samples showed the least PCS (group-G, 1.94) and DC (group-N, 0.53) values in their respective categories. PCS significantly decreased with delayed photo-initiation. A significant increase in DC was noticed when photo-initiation was delayed in the dual cure resin luting agent.