Abstract
The effect of cooling rate from solution heat treatment on the response to elevated temperature age-hardening of many technical and commercial magnesium-silicide alloys was determined in terms of a full range of cooling rates and tensile properties. The effect of individual minor element additions on the relationship was determined and an interpretation made in terms of the microstructure. From the data obtained it is possible to specify the precise cooling rate or combination of cooling rate and ageing procedure necessary to achieve a desired level of tensile properties. Where the mass of the metal places a limitation on the cooling rate the data make it possible to consider alternative alloys or additions to meet the tensile requirements.
Résumé
Les effets de la vitesse de trempe à partir du traitement de mise en solution sur le vieillissement à haute température d'un certain nombre d'alliages commerciaux ou synthétiques Aluminium - Magnésium - Silicium ont été étudiés par mesure des propriétés mécaniques en traction. L'auteur a étudié l'effet d' éléments d'addition mineurs sur la relation vitesse de trempe-propriétés mécaniques et présente une interprétation basée sur la microstructure.
A partir des résultats obtenus, il est possible de déterminer avec précision la vitesse de trempe ou la combinaison vitesse de trempe-conditions de vieillissement, nécessaires pour obtenir des propriétés mécaniques données. Lorsque la masse de métal impose une limitation à la vitesse de trempe, les résultats expérimentaux permettent de sélectionner d'autres alliages ou les additions nécessaires pour obtenir les propriétés mécaniques requises.