Abstract
The current-voltage (J-E) isotherms of single crystal FeSe0.5Te0.5 sample have been measured at several temperatures near the transition temperature (Tc) and under applied magnetic fields (H). A power law (E ∼ Jβ) has been used to fit the data and evaluate the activation energy Uo (T) using β = Uo/kBT. At low current density (J << Jc), the initial behaviour is associated with thermally activated flux Flow (TAFF) while at J >> Jc vortex flux flow (FF) behavior is expected. The effects of applied magnetic field on FF and TAFF also been investigated. We found that Uo(FF) was reduced with by about an order of magnitude in magnetic fields as low as ∼1.5 Tesla-the reduction in Uo(TAFF) is even faster than in Uo(FF)-hence reflecting the low pinning nature (defects, vacancies etc.) of FeSe0.5Te0.5 superconductor.