Abstract
This article presents a detailed analysis of beta ray exposed thermoluminescence response of a series of Eu3+ doped (0.5–10 mol%) Mg2SiO4 nanocrystalline samples successfully synthesized through solid state reaction method. Optimizing the doping concentration of Eu3+ ion in Mg2SiO4 phosphor was found as 3 mol%. Two main peaks were seen at 246 °C and 374 °C and also low temperature peak at 78 °C. The intensities of these peaks were increased linearly with increasing beta absorbed dose. Tm−Tstop method was used to reveal trap levels. Variable heating rate and computerized glow curve deconvolution methods were also used to evaluate the number of peaks and kinetic parameters, namely activation energy and frequency factor. The results of a series of experiments carried out to investigate some fading characteristics of Mg2SiO4:Eu3+ were also presented. The findings suggest that thermoluminescence properties of Mg2SiO4:Eu3+ makes this material suitable and promising dosimetric phosphor material for medical applications.
[Display omitted]
•Mg2SiO4 phosphors doped with Eu were synthesized by solid state reaction method.•Thermoluminescence properties were conducted.•Optimum doping concentration was 3 mol%.•Activation energies were calculated using Peak shape, VHR and CGCD method.