Abstract
The electrical transport properties were investigated of a glass system of basic composition 50 mol. % Pb(3)O(4)-50 mol. % P(2)O(5) containing CoO, Cr(2)O(3) or V(2)O(5) dopanys. The ac conductivity and the thermoelectric power were measured as a function of temperature. Properties such as dielectric constant, loss factor tangent and electrical conductivity are reported in the frequency range 200 Hz-100 kHz and temperature range 300-450 K. The variation in electrical conductivity with temperature was found to depend on the types of transition metal ions involved. The temperature dependence of the frequency exponent, s, was analyzed using different theoretical models. The variation of the thermoelectric power with temperature indicated the presence of more than one conduction mechanism for the investigated samples. This result was confirmed with the results of the dielectric properties at different frequencies. The introduction of cobalt ions in glass formers improves the electrical properties of non-crystalline ionic conductors.