Abstract
The fabrication of low-cost and mechanically robust flexible electronic patterns has increasingly gained attention due to their growing applications in flexible displays, touch screen panels, medical devices, and solar cells. Such applications require cost-effective deposition of metals in a well-controlled manner potentially using nanoparticles (NPs). The presence of solvent and precursors in NP based inks impacts the electrical conductivity of the printed pattern and a post-processing heating step is typically performed to restore the electrical properties and structure of the material. We report printing with picolitre droplet volumes of silver (Ag) NPs on flexible substrates using an acoustic microdroplet dispenser. The low-cost, controlled deposition of Ag ink is performed at room temperature on photopaper, polyimide and clear polyimide substrates. A localized, ultrashort pulsed laser with minimal heat affected zone is employed to sinter printed Ag patterns. For comparison, oven sintering is performed, and the results are analysed with scanning electron microscopy, four-point probe and Hall measurements. The femtosecond laser sintering revealed highly organized, connected nanostructure that is not achievable with oven heating. A significant decrease in sheet resistance, up to 93% in Ag NPs on clear polyimide confirms the laser sintering improves the connectivity of the printed film and as a result, the electrical properties are enhanced. The surface morphology attained by the laser sintering process is interpreted to be due to a joining of NPs as a result of a solid-state diffusion process in the near surface region of NPs.