Abstract
Glasses in the 90Bi(2)O(3)-(10-x)Er2O3-xPbO (x = 3, 5, 7, 9 and 10 mol%) system have been prepared by the melt-quenching technique. Elastic properties and FT-IR spectroscopic studies have been employed to study the role of PbO in the structure of the investigated system. Elastic properties and Debye temperature were recorded using sound wave velocity measurements at 4MHz at room temperature. The results showed that density increased and molar volume decreased, while both sound velocities increased with an increase in x. Infrared spectra of the glasses revealed that the bismuthate network is affected by an increase in PbO content. The results are interpreted in terms of the conversion of [BiO6] into [BiO3] structural units, indicating that Pb ions have been substituted for erbium ions as tetrahedral network formers. The elastic moduli increased with increasing PbO content due to the increased average bond strength and degree of connectivity, as a direct effect of the increase in [BiO3] structural units.