Abstract
Pongamia oil (PO) was converted to Pongamia oil hydroxyl (POH) via epoxidation process. The esterification of POH with linolenic acid was carried out to form hyperbranched polyester (HBPE), and further styrenation was performed at the conjugated double bond in the chain of linolenic acid. After styrenation, silver nanoparticle was added in different weight percentages (0.1-0.4 wt%). The structural elucidation of POH, HBPE, and HBPE-St was carried out by FT-IR, H-1-NMR, and C-13-NMR spectroscopic techniques. Physicochemical and physicomechanical analyses were performed by standard method. Thermal behavior of the HBPE-St was analyzed by using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The coatings of HBPE-St were prepared on mild steel strips. The anticorrosive behavior of HBPE-St resin-based coatings in acid, saline, and tap water was evaluated, and the molecular weight of HBPE-St was determined by gel permeation chromatography (GPC). The antibacterial activities of the HBPE-St copolymers were tested in vitro against bacteria and fungi by disc diffusion method. The HBPE-St copolymers exhibited good antibacterial activities and can be used as antimicrobial and corrosion-resistant coating materials.