Abstract
Local structural changes are studied occurring during transformation from amorphous to nanocrystalline phases of Fe sub 85 Zr sub 7 B sub 6 Cu sub 2 , Fe sub 73.5 Cu sub 1 Nb sub 3 Si sub 15.5 B sub 7 and Fe sub 66 Cr sub 8 Cu sub 1 Nb sub 3 Si sub 13 B sub 9 alloys. The nanocrystalline state of a formerly amorphous alloy was achieved by heat treatment at temperatures between 420 and 600 deg C. The high-resolution transmission electron microscopic images have shown the average size of the Fe and Fe(Si) nanograins in nanocrystalline alloys ranging from 5 to 15 nm in alloys at different stages of crystallization. X-ray absorption spectra at the K-edge of Fe, Cu and Cr atoms for nanocrystalline alloys measured using synchrotron radiation have shown a different local structure, namely the structure bcc Fe around Fe atoms, fcc Cu around Cu atoms and amorphous around Cr atoms. The growth of fcc Cu clusters before the nucleation of bcc Fe grains in nanocrystalline alloys was observed. It can be considered as a basic mechanism responsible for nanocrystalline grain formation. The FEFF8 program was used for calculations of X-ray absorption spectra up to about 260 eV above the Fe K-edge for bcc Fe metal and Fe sub 3 Si compound in terms of self-consistent muffin-tin potential approximation and full multiple scattering approach. The theoretical spectra well explained the experimental result that the amplitude of EXAFS oscillations in Fe sub 3 Si was considerably decreased by the presence of Si atoms in comparison to that for Fe metal.